Additively manufactured oxide dispersion strengthened nickel-based superalloy with superior high temperature properties
点击次数：
影响因子：
10.6
DOI码：
10.1080/17452759.2020.1848283
所属单位：
中南大学粉末冶金研究院
发表刊物：
Virtual and Physical Prototyping
项目来源：
国家科技重大项目（2017-VI-0008-0078），中国国家自然科学基金（NSFC）（91860105，52074366），中国博士后科学基金会（2019M662799）
关键字：
3-Dimensional printing, oxidenickel-based superalloy, hot extrusion, anisotropy
摘要：
With excellent radiation resistance and high temperature strength, the oxide dispersion strengthened (ODS) nickel-based superalloys are deemed as candidate materials for advanced fission and fusion reactor. Since conventional manufacturing processes are difficult to produce components with complex shapes, additive manufacturing becomes an alternative method. In this work, ODS nickel-based superalloy was manufactured by laser metal deposition (LMD) technology using mechanically alloyed powder. The microstructure and high temperature mechanical properties of the as-deposited alloy were analysed. The results indicated that the as-deposited alloys prepared by this method owned anisotropic structure and uniformly distributed high-density oxides, contributing to superior high-temperature performance, in comparison with the samples produced by LMD using pre-alloyed powder and traditional hot extrusion.
合写作者：
Guowei Wang, Yu Guo, Qihong Fang, Zecheng Liu, Xiangyou Xiao, Wuqiang He, Zijun QinORCID Icon, Yong Zhang, Lan Huang
第一作者：
谭黎明
论文类型：
Article
通讯作者：
Feng Liu
学科门类：
工学
一级学科：
冶金
卷号：
15
页面范围：
555-569
ISSN号：
1745-2759
是否译文：
否
学位：博士学位
职称：副研究员
学科：材料科学与工程
所在单位：粉末冶金研究院