Evolution of LPSO phases in a Mg-Zn-Y-Gd-Zr alloy during semi-continuous casting, homogenization and hot extrusion
发布时间：2021-10-21
点击次数：
DOI码：10.1016/j.matdes.2018.04.070
发表刊物：Materials & Design
关键字：Magnesium alloy; LPSO phase; Stacking faults; Extrusion; Recrystallization (DRX)
摘要：A large size Mg-1.2Zn-3.4Y-4.7Gd-0.5Zr (wt%) alloy sheet was manufactured by semi-continuous casting, homogenization and hot extrusion, in which the microstructures were systematically examined. The results showed that: (i) During homogenization, the generation of 14H LPSO phase was mainly achieved by two phase transition processes of “Mg5(Gd,Y,Zn) phase → 14H LPSO phase” and “18R LPSO phase → 14H LPSO phase”. (ii) During extrusion, the evolution of LPSO phases with various morphologies was driven by severe deformation and dynamic recrystallization (DRX). Under severe deformation, the 14H LPSO phases in homogenized alloy were broken down to fragments with various sizes. Under the influence of DRX, the deformation defects of small LPSO fragments were fully eliminated and formed the “sandwich-like” LPSO phase. While the deformation defects of coarse LPSO fragments were less eliminated and formed the “irregular-shaped” LPSO phase. Meanwhile, due to the decreased solubility of Zn, Y and Gd in the extruded alloy matrix, the solution elements of Zn, Y and Gd were impelled to precipitate at the scattering arranged stacking faults (SFs) and formed the “needle-like” LPSO phase. It is found that the gliding of Shockley partial dislocation(s) on basal plane was structurally needed during the precipitation of needle-like LPSO phase.
合写作者：Z.Y. Chen*, J.B. Shao, R.K. Wang, L.H. Mao, C.M. Liu
第一作者：T. Chen
论文类型：期刊论文
学科门类：工学
一级学科：材料科学与工程
文献类型：J
卷号：152
页面范围：1-9
ISSN号：0264-1275
是否译文：否
发表时间：2018-04-28
收录刊物：SCI