Microstructure, texture and mechanical properties of Mg-Gd-Y-Zr alloy annular forging processed by hot ring rolling
- 点击次数：
- 影响因子：5.234
- DOI码：10.1016/j.msea.2017.02.036
- 发表刊物：Materials Science and Engineering: A
- 关键字：Magnesium alloyHot ring rollingMicrostructureTextureMechanical anisotropy
- 摘要：Hot ring rolling (HRR) was successfully applied to fabricate large-size seamless magnesium alloy annular forging in this work and the resultant microstructures, texture and mechanical properties of the ring are discussed. Results show that the microstructures, along the thickness direction of the ring, are heterogeneously distributed, with the extent of dynamic recrystallization (DRX) differing among different sampling regions, owing to the inhomogeneous strain and temperature distribution. Typical basal texture is identified in all sampling regions, but with different degree of inclination or scattering of the {0002} basal poles. Due to the rotation of the basal poles towards some specific direction, the ring exhibits an obvious mechanical anisotropy. After aging treatment, the best comprehensive mechanical properties are obtained in the transverse direction of the outer region, with an ultimate tensile stress of 456 MPa, yield stress of 426 MPa and elongation to failure of 3.5%.
- 合写作者：Chuming Liu, Shunong Jiang
- 第一作者：Shilun Yu
- 通讯作者：Yonghao Gao
- 论文编号：WOS:000397698600006
- 学科门类：工学
- 一级学科：材料科学与工程
- 文献类型：J
- 卷号：689
- 页面范围：40-47
- ISSN号：0921-5093
- 是否译文：否
- 发表时间：2017-03-24
- 收录刊物：SCI、EI