Dynamic recrystallization mechanism of Mg-8.5Gd-2.5Y-0.4Zr alloy during hot ring rolling
发布时间：2021-07-12
点击次数：
影响因子：4.342
DOI码：10.1016/j.matchar.2017.07.015
发表刊物：Materials Characterization
关键字：Magnesium alloys; Hot ring rolling; Dislocations; Dynamic recrystallization; TEM
摘要：Dynamic recrystallization (DRX) behavior of Mg-8.5Gd-2.5Y-0.4Zr alloy subjected to hot ring rolling was investigated in this paper. Three different DRX mechanisms were identified based on TEM: "fragmentation" of lamellar structures, transformation of subgrains separated by dislocation arrays, and strain-induced boundary bulging mechanism. Therein, the first one is a novel mechanism that has not been reported before in magnesium and its alloys. Preliminary analysis suggests that this mechanism might result from the high strain rate and continuous repeated rolling deformation provided by hot ring rolling.
合写作者：Chuming Liu, Shunong Jiang, Zhangqi Bao
第一作者：Shilun Yu
通讯作者：Yonghao Gao
论文编号：WOS:000411535600015
学科门类：工学
一级学科：材料科学与工程
文献类型：J
卷号：131
页面范围：135-139
是否译文：否
发表时间：2017-09-01
收录刊物：SCI、EI