Influence of finish rolling temperature on the microstructure and mechanical properties of Mg-8.5Al-0.5Zn-0.2Mn-0.15Ag alloy sheets
发布时间：2021-07-12
点击次数：
影响因子：4.342
发表刊物：Materials Characterization
关键字：Magnesium alloy; Hot rolling; Microstructure; Shear zones; Anisotropy
摘要：Mg-8.5Al-0.5Zn-0.2Mn-0.15Ag (wt%) magnesium sheets were produced with various final rolling temperatures, and their microstructures and mechanical properties were characterized. It was found that low final rolling temperature (LT) resulted in stronger heterogeneity, stronger basal texture and higher strength compared with the high final rolling temperature (HT). Considerable shear zones were observed within both the LT and HT sheets, even though their microstructures, formation mechanisms and mechanical properties were different. Preliminary analysis suggests that the shear zones exert great influence on the mechanical anisotropy of whole sheets.
合写作者：Chuming Liu, Shunong Jiang, Yunfeng Liu
第一作者：Li Cao
论文类型：期刊论文
通讯作者：Yonghao Gao
论文编号：WOS:000431469300005
学科门类：工学
一级学科：材料科学与工程
文献类型：J
卷号：139
页面范围：38-48
ISSN号：1044-5803
是否译文：否
发表时间：2018-05-01
收录刊物：EI、SCI