颜志梁论文“Co3O4/Co nanoparticles enclosed graphitic carbon as anode material for high performance Li-ion batteries”被Chemical Engineering Journal 接收发表
发布时间：2020-04-25
点击次数：
The composite of Co3O4, Co and graphitized carbon is synthesized by carbonization and cobalt-catalyzed-graphitization of carboxymethyl chitosan, followed by low-temperature thermal oxidation. At the high temperature, the Co(+2) is reduced to metallic Co and the produced Co acts as a catalyst for the graphitization of the pyrolytic carbon. The low-temperature oxidation is conducted to selectively oxidize Co to Co3O4 while the carbon remains unreacted. The sample is characterized by XRD, SEM and TEM techniques. The structure analysis indicates that three crystal phases (graphite, metallic Co, Co3O4) accompanied with amorphous carbon are co-existed in the composite. Morphological results demonstrate that a lot of graphite grains around the Co element are distributed in the carbon. The electrochemical testing results indicate that the composite shows good electrochemical performance. It delivers a reversible capacity of 843 mAh g-1 at low current density, and remaining 88.9% after 60 cycles at 200 mA g-1. Even performed at 1 A g-1, it also exhibits 493 mAh g-1. The performance improvement is mainly due to the high capacity of Co3O4, high conductivity of graphitic carbon and metallic cobalt, the porous structure offering enough ion transport pathways and relieving the strain during cycling.