Reduction behavior of SnO2 in the tin-bearing iron concentrates under CO-CO2 atmosphere. Part I: Effect of magnetite

发布时间:2016-07-05

点击次数:

所属单位:School of Minerals Processing and Bioengineering, Central South University

发表刊物:Powder Technology

关键字:Tin-bearing iron concentrate; Cassiterite; Reduction volatilization; Fe–Sn spinel

摘要:A selective reduction volatilization (SRV) process developed by the authors could remove excessive tin from the complex tin-bearing iron concentrates. But it was especially noteworthy that the volatilization ratio of Sn and the residual tin content were obviously influenced by the variation of roasting parameters during the SRV process. Hence, the existence form of residual tin in the roasted products and the possible reactions between SnO2 and Fe3O4 need to be further determined. In the present study, the effect of roasting parameters on the reduction of SnO2 in the tin-bearing iron concentra

合写作者:Guanghui Li, Tao Jiang, Youlian Zhou, Bingbing Liu, Yuanbo Zhang*, Zijian Su

论文类型:基础研究

学科门类:冶金工程学

文献类型:J

卷号:292

页面范围:251-259

是否译文:

发表时间:2016-01-05

发布期刊链接:http://www.sciencedirect.com/science/article/pii/S0032591015302576

附件:

  • Reduction behavior of SnO2 in the tin-bearing iron concentrates under CO-CO2 atmosphere. Part I_ Effect of magnetite.pdf

  • 上一条: Reduction behavior of SnO2 in the tin-bearing iron concentrates under CO-CO2 atmosphere. Part II:Effect of quartz

    下一条: Volatilization behavior of SnO2 reduced under different CO-CO2 atmospheres at 975°C-1100°C