Effect of aging temperature on precipitation behavior and mechanical properties of extruded AZ80-Ag alloy
- 点击次数：
- 影响因子：5.316
- DOI码：10.1016/j.jallcom.2015.06.126
- 发表刊物：JOURNAL OF ALLOYS AND COMPOUNDS
- 关键字：Magnesium alloyAZ80-AgAging behaviorMicrostructural evolutionPrecipitatesMechanical properties
- 摘要：Aging behavior and related microstructural evolution of AZ80-Ag alloy as a function of aging temperature are systematically investigated. Results show that Ag addition can significantly enhance the age-hardening response of AZ80, improving its peak hardness and shortening the time to reach the peak simultaneously. Two kinds of continuous precipitates and three kinds of discontinuous precipitates are observed under varying conditions. The volume fraction ratio of continuous precipitates to discontinuous precipitates increases with increasing aging temperature. When aged at 175 degrees C for 38 h, the whole microstructure is invaded by discontinuous precipitates and an ultimate tensile strength of 428 MPa is achieved.
- 合写作者：Chuming Liu, Xiuzhu Han
- 第一作者：Shilun Yu
- 论文类型：期刊论文
- 通讯作者：Yonghao Gao
- 论文编号：WOS:000361153700065
- 学科门类：工学
- 一级学科：材料科学与工程
- 文献类型：J
- 卷号：646
- 页面范围：431-436
- ISSN号：0925-8388
- 是否译文：否
- 发表时间：2015-10-15
- 收录刊物：SCI、EI