Effects of hot ring rolling and aging treatment on microstructure and mechanical properties of AZ80-Ag alloy
发布时间：2021-07-12
点击次数：
影响因子：5.234
DOI码：10.1016/j.msea.2015.08.032
发表刊物：Materials Science and Engineering:A
关键字：AZ80-AgHot ring rollingMicrostructureTextureMechanical anisotropy
摘要：For the first time, a large sized AZ80-Ag alloy ring was successfully manufactured by hot ring rolling (HRR) at 673 K. The effects of the HRR process and aging treatment on microstructure, texture and mechanical properties were systematically investigated. The microstructure is mainly composed of the equiaxed grains, suggesting the occurrence of dynamic recrystallization. After aging at 448 K for 36 h, considerable discontinuous fl-MgvAliz precipitates with a small number of continuous beta-Mg17Al12 phase. Ag is mainly segregated in the beta-Mg17Al12 precipitates. The yield strength along the axial direction is higher than that along the rolling direction, indicating obvious mechanical anisotropy due to the inclination of {0002} basal pole towards the rolling direction. After aging treatment, the yield strength and ultimate tensile strength are enhanced owing to the precipitation of beta-Mg17Al12 phase.
合写作者：Shilun Yu, Chuming Liu, Xiuzhu Han
第一作者：Gang Zeng
通讯作者：Yonghao Gao
论文编号：WOS:000361581900033
学科门类：工学
一级学科：材料科学与工程
文献类型：J
卷号：645
页面范围：273-279
ISSN号：0921-5093
是否译文：否
发表时间：2015-10-01
收录刊物：SCI、EI