Superplastic behavior of a powder metallurgy superalloy during isothermal compression

发布时间:2019-12-06

点击次数:

影响因子:10.9

DOI码:10.1016/j.jmst.2019.05.025

所属单位:中南大学粉末冶金研究院

教研室:高温结构材料研究所

发表刊物:Journal of Materials Science & Technology

项目来源:中国国家重点研究与发展计划(No.2016YFB0701404),中国国家自然科学基金(91860105)和广东省引进的创新与企业家团队基金(201301G0105337290)

关键字:Nickel-based superalloy, Superplastic deformation, Dynamic recrystallization, Grain boundary sliding, Hot compression

摘要:In this work, the flow behaviors and microstructure evolution of a powder metallurgy nickel-based superalloy during superplastic compression is investigated. Based on the strain rate sensitivity m determined by flow data, superplastic region is estimated at relatively low temperature and strain rate domains, specifically around 1000 degrees C/10(-3)s(-1). Thereafter, the cylinder specimens are isothermally compressed at 1000 degrees C/10(-3)s(-1) and 1025 degrees C/10(-3)s(-1) with different strains, to exam the superplasticity and related mechanisms. The experimental results indicate that the accumulated dislocations are mainly annihilated by dynamic recovery and dynamic recrystallization (DRX), and the grain boundary sliding (GBS) contributes to the total strain during superplastic compression as well. In addition, the cavities and cracks at triple junctions or interfaces between matrix and second phase particle have not been detected, which is different from superplastic tensile deformation. (C) 2019 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

合写作者:Yunping Li, Yan Nie, Liang Jiang

第一作者:谭黎明

论文类型:Article

通讯作者:Feng Liu

学科门类:工学

一级学科:冶金

卷号:35

页面范围:2591-2599

ISSN号:1005-0302

是否译文:

发表时间:2019-12-06

上一条: Mechanism of grain refinement in an equiatomic medium-entropy alloy CrCoNi during hot deformation

下一条: Microstructure evolutions of a powder metallurgy superalloy during high-strain-rate deformation